Phenolic Beads, Hollow

Referentie 17806-100

Formaat : 100g

Merk : Polysciences

Meer informatie aanvragen

Neem contact op met een lokale distributeur :


Telefoonnummer : +1 850 650 7790

Phenolic Beads, Hollow

Grouped product items
Catalog Number Unit Size QTY
17806-100 100 g

Product Overview

In many uses of liquid resins, it is desirable to reduce the weight of the finished product. One way to reduce the weight below the original resin weight is to incorporate a suitable additive. Hollow phenolic microspheres are excellent for use in a variety of industrial applications. They are lightweight, chemically inert, and mechanically strong. They can be excellent adhesives, gap filling formulations, sandable putties, syntactic foams, and molded and laminated structures that must be lightweight and strong. About 30% by weight will make most resins unpourable. Filling casting are quite machinable; turns casting brown.

Composition: Phenolic resin (Phenol formaldehyde resin)

Nominal Reference Values

Size Range: 5 - 127µm

Bulk Density: 0.104 g/cm3, max; 6.5 lb/ft3, max

Relative Density: 0.20 - 0.80 g/cm3

Average Hydrostatic Compressive Strength: 350psi

Application(s):
General use

Properties

Tg:
200 - 220° C
Solubility:
Insoluble in water
Appearance:
Red brown powder, ordorless
Glass Transition Temperature, Tg (ºC):
200 - 220° C
Concentration (nom.):
100% solids (dry)

Related Documents

References

Yusriah, L., Mariatti, M., & Abu Bakar, A. (2010). The properties of vinyl ester composites reinforced with different types of woven fabric and hollow phenolic microspheres. Journal of Reinforced Plastics and Composites, 29(20), 3066-3073.

Rutz, B. H., & Berg, J. C. (2010). A review of the feasibility of lightening structural polymeric composites with voids without compromising mechanical properties. Advances in Colloid and Interface Science, 160(1-2), 56-75.

Wouterson, E. M., Boey, F. Y., Hu, X., & Wong, S. C. (2007). Effect of fiber reinforcement on the tensile, fracture and thermal properties of syntactic foam. Polymer, 48(11), 3183-3191.

Safety & Storage